Product Description
Used magnesia chrome fire brick for refractory recycle
Magnesium chrome brick magnesia (MgO) and chromium oxide (Cr2O3) as the main ingredient, periclase and spinel as the main mineral components of refractory products. Such brick high refractoriness, high temperature strength, resistance to basic slag erosion resistance, excellent thermal stability, acidic slag also has some adaptability. The main raw material to manufacture magnesium chrome brick is sintered magnesia and chromite. Purity magnesia raw material to be as high as possible, the requirements of the chemical composition of chromite is: Cr2O3: 30 ~ 45%, CaO1.0 ~ 1.5%.
Category
Used magnesia chrome fire brick for refractory recycle
Fused re-bonded magnesia chrome brick:
The magnesia chrome refractory for RH refining device developed by the Company has the characteristics of high purity.high fire resistance and good thermal stability.It’s applicable to large.medium and silicon steel RH refining devices, This project is tested on the RH silicon steel device in Wuhan lron & Steel.and the tested service life was increased by 20%.
The burnt magnesia chrome bricks are made out of high-quality magnesite and chrome ore fine charge mixture.According to different demands,adjust the content of Cr2O3,The product thermal stability and high-temperature performance are satisfactory,It’s widely used in the cement kiln and nonferrous metallurgical furnace etc.
1.Direct bonding magnesia chrome bricks choose the raw materials of chrome ore with low impurity content and magnesite with high quality and high purity,and adopt the high-pressure forming and over 1700℃ high-temperature sintering.The high-temperature performance is satisfactory,and the metallurgical slag corrosion resistance is strong.It can resist the corrosion of cement clinker,It’s widely applied in the electric furnace lining for steel making,nonferrous metallurgical furnace and cement rotary kiln etc.
2.The semi-rebonded magnesia chrome bricks and rebonded magnesia chrome bricks all or partially use the fused sand(fused synthetic clinker)as the raw materials,choose the fine charge mixture and adopt the high-pressure forming and super-high-temperature burning.The products have good particle bonding degree,high product strength and good volume stability.They are widely used in the secondary refining devices like RH,VOD and AOD,and nonferrous metallurgical furnace as well.
Feature
Used magnesia chrome fire brick for refractory recycle
Description of magnesia chrome bricks
High strength
Corrosion resistance
Erosion resistance
Excellent slag resistance
Good thermal shock stability
Advantage of magnesia chrome bricks
The directly bonded magnesia-chrome brick has high temperature resistance, good corrosion resistance, thermal shock resistance and bulk stability under high temperature etc.
Technical Data
Used magnesia chrome fire brick for refractory recycle
Chemical & Physical Data Of Magnesia Chrome Bricks
| Brand | MgO % | Cr2O3 % | SiO2 % | A.P. % | BDg/cm3 | CCS.MPa | R.U.L ℃ |
| LADBMGe-8A | ≥74 | ≥8 | ≤1.5 | ≤18 | 2.98 | ≥40 | 1660 |
| LADBMGe-8B | ≥74 | ≥8 | ≤2.0 | ≤18 | 2.98 | ≥35 | 1600 |
| LADBMGe-12A | ≥66 | ≥12 | ≤1.5 | ≤18 | 3.1 | ≥40 | 1660 |
| LADBMGe-12B | ≥66 | ≥12 | ≤2.0 | ≤18 | 3.1 | ≥35 | 1600 |
| LADBMGe-16A | ≥60 | ≥16 | ≤1.5 | ≤18 | 3.15 | ≥40 | 1660 |
| LADBMGe-16B | ≥60 | ≥16 | ≤2.0 | ≤18 | 3.15 | ≥35 | 1600 |
Main Application:It’s mainly applied to line the sintering zone of the new dry-processing of cement kilns and glass tank furnaces as checkers and the other industrial furnaces.
| Brand | MgO % | Cr2O3 % | SiO2 % | A.P. % | BDg/cm3 | CCS.MPa | R.U.L ℃ |
| LARBMG-16A | ≥65 | ≥16 | ≤1.2 | ≤16 | 3.1 | ≥45 | 1750 |
| LARBMG-16B | ≥60 | ≥16 | ≤1.6 | ≤16 | 3.1 | ≥40 | 1700 |
| LARBMG-20A | ≥60 | ≥20 | ≤1.2 | ≤16 | 3.15 | ≥45 | 1750 |
| LARBMG-20B | ≥60 | ≥20 | ≤1.2 | ≤16 | 3.15 | ≥40 | 1700 |
Main Application:It’s suitable for lining of the slag zone area of refining furnaces of VOD,SKF.
| Brand | MgO % | Cr2O3 % | SiO2 % | A.P. % | BDg/cm3 | CCS.MPa | R.U.L ℃ |
| LASBMG-16A | ≥60 | ≥16 | ≤1.5 | ≤17 | 3.1 | ≥40 | 1750 |
| LASBMG-16B | ≥60 | ≥16 | ≤1.8 | ≤17 | 3.1 | ≥35 | 1700 |
| LASBMG-20A | ≥55 | ≥20 | ≤1.5 | ≤17 | 3.15 | ≥40 | 1750 |
| LASBMG-20B | ≥55 | ≥20 | ≤1.8 | ≤17 | 3.15 | ≥35 | 1700 |
Main Application:It’s widely used for every industrial furnaces of the metallurgical and building materials industry.
Packaging & Shipping
Used magnesia chrome fire brick for refractory recycle
Production Process
Used magnesia chrome fire brick for refractory recycle
1)Raw material to factory→checkout→burdening→stirring→mixing→taking out the raw material,
2)Crushing→Mixing→Shaping→Drying→Firing→Inspection→Packaging and Shipment.
2.Quality Assurance
1)Going out the furnace→checkout→packing→qualified product→putting in storage→sale,
2)The process from raw to product are strictly tested by equipment.
1.Inspection and Control of incoming raw materials: according to the chemical content,raw materials are classified into different levels to ensure quality of brick first.
2.Inspection and control of the process: during the production,every brick will be weighed twice strictly to reduce the error of weight .
3.Quality audit by quality management: inspection of product standardization of quality of each product by process control and experimentation, taking corrective measures timely whenever deviations are noted.
4.Before delivery, the inspectors will inspect the size,appearance, physical and chemical properties of magnesia chrome bricks again in factory.
contact
Used magnesia chrome fire brick for refractory recycle
- Competitive Price. Make the products competitive in your market.
- Abundant Experience. Prevent cracks and twist in bricks.
- Different Moulds. Save mould fees for you.
- Strict Quality Control. Meet clients’ quality requirement.
- Large stocks. Guarantee prompt delivery.
- Professional Packing. Avoid damage and secure the goods in transportation